N08120/ HAYNES HR120 Alloy- TJC STEEL.

N08120 Alloy/ HAYNES HR120 is one kind of alloys with extremely high temperature strength and anti-carburizing and anti-curing. N08120 Alloy has good resistance to industrial environment performing with solid solution strengthened heat resistant. Besides, this alloy offers excellent oxidation resistance and is comparable to any of the widely used Fe-Ni-Cr alloys, such as 300 series stainless steel, 800H [TJC STEEL]and 800HT.  Its strength is significantly higher at 1095°C, even compared to ni-Cr alloy.  N08120 Alloy/ HAYNES HR120 can be formed by cold and hot processing. When welding, Hastelloy X or HAYNES 556 cases are selected as welding materials according to the performance requirements.  
 
N08120/ HAYNES HR120 Alloy’s oxidation resistance is comparable to that of other widely used Fe-Ni-Cr materials (such as 330 and 800H alloys), but still has high strength at temperatures up to 2000ºF (1095ºC) degrees.  [TJC STEEL]It is significantly higher even when compared to Ni-Cr alloy.  The alloy is usually welded using a HAYNES 556 filler wire.  

Chemical Composition（%）
C（%）：0.02~0.10
Si（%）：≤1.00
Mn（%）：≤1.50
P（%）≤：0.035
S（%）≤：0.030
Cr（%）：23.0~27.0
Ni（%）：35.0~39.0
Mo（%）：≤2.50
Nb（%）：0.40~0.90
Ti（%）：≤0.20
Cu（%）：≤0.50
Al（%）：≤0.40
N（%）：0.15~0.30
B（%）：≤0.010

Physical Property：

GRADE DATA
HAYNES HR120 ROOM TEM 1000℃
DENSITY 8.07
MELTING POINT/℃ 1300
THERMAL CONDUCTIVITY/[W/(m.k)] 11.4 28
THERMAL DIFFUSION /(cm²/s) 30.4*0.01 50.7*0.01
MASSIC HEAT CAPACITY/[J(KG.K][TJC STEEL] 476 663
ELASTICITY MODULUS/GPa 197 128
THERMAL EXPANSIVITY /[m/(M.℃] 14.3 17.8

Mechanical Property：
GRADE DATA/MPa
HAYNES HR120 ROOM TEM 1000℃
TENSILE STRENGTH 734 104
YIELD STRENGTH[TJC STEEL] 314 62.7
ELONGATION 50% 89%