​5086 aluminum alloy is mainly used in ships, automobiles and aircraft plate weldable parts, etc.
Chinese name 5086 aluminum alloy[TJC STEEL] standard: GB/T 4437.1-2000 Aluminum Al: residual silicon Si: ≤0.40 copper Cu: ≤0.10
 
Overview of 5086 Aluminium Alloy
Aluminum-magnesium alloy and aluminum-manganese alloy are collectively referred to as anti-rust aluminum, because the alloy [TJC STEEL]composition between them can increase their anti-corrosion properties. The representative of aluminum-manganese alloy is 3003,3004,3105. According to the magnesium alloy content, the order is 5005, 5252, 5251, 5050, 5052, 5754, 5083, 5056, 5086 and so on. 5086 aluminum plate typical use: for the need to have high corrosion resistance, good weldability and medium strength occasions, such as the need for strict fire pressure vessels, refrigeration devices, TV towers, installation of exploration equipment, transportation equipment, missile parts, armor, etc.
5086 aluminum plate supply status: O, H112,[TJC STEEL] H116, H111, H321, H32, H36, H38
 
Chemical Composition for 5086 Aluminium Alloy
Silicon :0.00 to 0.40
Iron Fe: 0.000 ~ 0.500
Copper Cu:0.00 to 0.10
Magnesium Mg: 3.5 ~ 4.5
Zinc-zn: ≤0.25
Manganese Mn: 0.20 ~ 0.7
Ti: ≤0.15
Chromium Cr: 0.05 ~ 0.25[TJC STEEL]
Note: Single :≤0.05; Total :≤0.15
 
Mechanical Property of 5086 Aluminium Alloy
Tensile strength σb (MPa) : ≥240
Conditional yield strength σ0.2 (MPa) : ≥95
Elongation δ10 (%) : ≥10
Elongation δ5 (%) : ≥12
Note: longitudinal mechanical properties of pipe at room temperature
Sample size: all wall thickness[TJC STEEL]
State: Aluminum and aluminum alloy hot extrusion seamless round tube (H112 state)
 

5083 Aluminum Plate is a kind of high magnesium alloy.[TJC STEEL] It has good strength, corrosion resistance and machinability among non-heat treatment alloys.
 
5083 Aluminum Plate’s Features:
 
① The surface of 5083 aluminum plate is beautiful [TJC STEEL]after anodizing treatment. Good arc welding performance. The main alloying element in 5083 alloy is magnesium, which has good corrosion resistance and weldable properties, as well as moderate strength. Excellent corrosion resistance makes 5083 alloy widely used in Marine applications such as ships, as well as automobile, aircraft welding parts, subway light rail, strict fire pressure vessels (such as liquid tank cars, refrigerated trucks, refrigerated containers), [TJC STEEL]refrigeration units, TV towers, drilling equipment, transportation equipment, missile parts, armor, etc.
②5083 belongs to Al-Mg alloy, which is widely used, especially in the construction industry, it is the most promising alloy. Good corrosion resistance, excellent weldability, good cold workability, and moderate strength. The main alloy element of 5083[TJC STEEL] is magnesium, which has good formability, corrosion resistance, weldability and medium strength. It is used in the manufacture of aircraft fuel tanks, oil pipes, traffic vehicles, ships, sheet metal parts, instruments, street lamp brackets and rivets, hardware products, electrical shell and so on. (3) AL-Mg alloy, is the most widely used kind of antirust aluminum, this alloy has high strength, especially fatigue strength: high plasticity and corrosion resistance, can not be strengthened by heat treatment, in the semi-cold hardening plasticity is good, cold hardening plasticity is low, good corrosion resistance, good weldability, bad machinability, polishing. The utility is mainly used for requiring high plasticity and good weldability, low load[TJC STEEL] parts working in liquid or gas medium, such as oil tank, gasoline or lubricating oil conduit, various liquid containers and other small load parts made with deep drawing: wire used to do rivets.
 
Chemical Composition for 5083 Aluminum Plate:
Aluminum Al: allowance
Silicon Si: ≤0.40
Copper Cu: ≤0.10
Magnesium Mg: 4.0 ~ 4.9
Zinc-zn: ≤0.25
Manganese Mn: 0.40 ~ 1.0
Ti: ≤0.15
Chromium Cr: 0.05 ~ 0.25
Iron Fe: 0.000 ~ 0.400[TJC STEEL]
Note: Single :≤0.05; Total :≤0.15
Density: 2.71g/cm3
 
Mechanical Properties for 5083 High Magnesium Aluminum Alloy:
Conditional yield strength σ0.2 (MPa) : ≥110
Elongation δ10 (%) : ≥20
Elongation δ5 (%) : ≥12[TJC STEEL]
Note: longitudinal mechanical properties of pipe at room temperature