316Ti stainless steel plate is named 0Cr18Ni12Mo2Ti in international standard, and Chinese brand name is 1Cr18Ni12Mo2Ti stainless [TJC STEEL]steel plate, 316Ti stainless steel plate is added Ti element in SUS316 to improve the resistance to intergranular corrosion. 316Ti stainless steel is used for equipment to resist sulfuric acid, phosphoric acid, acetic acid and acetic acid.  
 
Physical Properties of 316Ti Stainless Steel:  
 
A.Chemical Composition(%):  
C: 0.08 or less  
Si 1.00 or less  
Mn 2.00 or less  
P 0.035 or less  
S 0.030 or less  
Ni 10.00 ~ 14.00 [TJC STEEL] 
Cr 16.00 ~ 19.00  
Mo 1.80 ~ 2.50  
Ti acuity 0.2 ~ 0.70  
GB/T1220-1992 has this provision, usually also called Mo2Ti or 316Ti  
 
B.Mechanical Properties:  
YS (Mpa) ≥205  
TS (Mpa) ≥520  
EL (%) ≥40  
Hv around 200 °  
Thickness: cold-tied 2B plate (0.09 -- 6.0mm);  
Hot rolled industrial plate No.1(3-50mm) [TJC STEEL]medium thick plate, chemical plate, high temperature plate;  
Width: 5mm-- 850mm steel belt;  
1000, 1219, 1250, 1500, 1800, 2000mm coil plate, plate  
Surface: 2B smooth surface, No.1 industrial surface, BA (6K) mirror, 8K mirror, 9K mirror, drawing surface, frosted surface.  
Origin: Domestic, imported (Sweden,[TJC STEEL] Japan, Finland, South Korea, South Africa, Taiwan)  
 
Key Properties of 316Ti Stainless:  
These attributes refer to products in similar, but not identical, attributes that are specified in other products, such as plates and forgings in their respective specifications.  The lower minimum pre - and post-heat[TJC STEEL] temperatures reduce the incidence of weld cracking and simplify welding.  Low hardness decreases the heat affected zone to minimize deterioration in mold performance.  

Introduction for 15NiMn6 Alloy Steel Plate:   
1.15NiMn6 Is a nickel alloy steel plate for [TJC STEEL]pressure applications. Standard: EN10028-4(Hot Rolled Type) or EN10222-3（Forged Type）.  
 
2.15NiMn6 Dimensions, Shape, Weight and Allowable Deviation   
The size, shape and allowable deviation of[TJC STEEL] the steel plate shall meet the requirements of 2007+ A1:2009 in EN10028-1.  
 
3.15NiMn6 Delivery Status   
3.1 15NiMn6 Steel Plates are normally delivered in normalizing, normalizing and tempering condition.   
3.2 Steel plates shall be delivered by [TJC STEEL]shearing or flame cutting   
4. Chemical Composition of 15NiMn6  
The chemical composition of nimN6 steel (melting analysis) shall meet the following requirements (%) :  
 
Chemical Composition Required for 15NiMN6 (%):  
C 0.18 or less;  Si 0.35 or less;  [TJC STEEL]Mn: 0.8-1.5;  P 0.025 or less;  S 0.015 or less;  Al:-;   Ni: 1.30-1.70;  V 0.05 or less.   
Elements not listed in this table shall not be intentionally added to steel without the consent of the demander, except after smelting, and all appropriate measures shall be taken during the steelmaking process to prevent the addition of [TJC STEEL]these elements from scrap and other materials which may adversely affect the mechanical properties and serviceability of the steel.  Among them: Cr + Cu + Mo 0.5 or less  
 
5.1 15NiMn6 Mechanical Performance:   
The mechanical and process properties of [TJC STEEL]NIMN6 shall comply with the following table:  
 
15NiMn6 mechanical requirements (transverse)   
Grade    Thickness    Yield strength (MPa)    Tensile strength (MPa)    Elongation A(%)  
 
15NiMn6   ≤30         ≥355                 490-640               ≥22  
 
15NiMn6   30-50        ≥345                 490-640               ≥22  
 
15NiMn6   50-80        ≥335                 490-640               ≥22