1Cr13, 410,1.4006 Martensitic Stainless Steel- TJC STEEL.

3/5/2021

 
​1Cr13 (410) stainless steel is one of the representative of martensitic stainless steel.Martensitic stainless steels are stainless steels [TJC STEEL]whose strength and properties can be improved by heat treatment.

Standard Control
CHINA GB/T  20878-2007 12Cr13(1Cr13)
AMERICA ASTM  A240-2015a S41000,410
JAPAN JIS  G 4303:2005 SUS410
GERMANY EN  10088-1:2005[TJC STEEL] X12C13,1.4006

Component Specification
GRADE 12Cr13 410 SUS410 1.4006
C ≤0.15 0.08~0.15 ≤0.15 0.08~0.15
Si ≤1.00 ≤1.00 ≤1.00 ≤1.00
Mn ≤1.00 ≤1.00 ≤1.00 ≤1.50
P ≤0.040 ≤0.040 ≤0.040 ≤0.040
S ≤0.030 ≤0.030 ≤0.030 ≤0.030
Cr 11.5~13.5 11.5~13.5 11.5~13.5 11.5~13.5
Ni (≤0.60) ≤0.75[TJC STEEL] (≤0.60) ≤0.75

Mechanical Property
density(g/cm3)20℃ 7.70
Melting point (℃) 1480~1530
Specific heat [kJ/(kg·K)]  0~100℃ 0.46
Heat conductivity [W/(m·K)][TJC STEEL] 100℃ 24.2
500℃ 28.9
coefficient of linear expansion(10-6/K) 0~100℃ 11.0
0~500℃ 11.7
specific resistance(Ω·mm2/m)20℃ 0.57
longitudinal modulus of elasticity(kN/mm2)20℃ 200
magnetism Y

Mechanical Property
Dimensions of sample hairs(mm) ≤75
heat treating regime anneal[TJC STEEL] 800 ~ 900 ℃slow cooling
Or about 750℃ fast cooling
quench 950~1000℃ cold oil
temper 700~750℃cold oil
Mechanical properties 
(quenching+tempering) Specified non-proportionality
Extension strength MPa ≥345
strength of extension MPa ≥540
Percentage elongation after fracture % ≥22
Percentagereduction of area; reduction of area  % ≥55
Impact absorption work J ≥78
The hardness of delivery HBW anneal ≤200
Quenching + tempering ≥159

Material characteristics:
As a martensitic stainless steel, 1Cr13 also obtains high strength and good toughness through quenching and tempering at high temperature.Bensteel is usually compared with 2Cr13, 3Cr13, 4Cr13, is the lowest carbon content [TJC STEEL]in the four grades, so the strength is the lowest, and the best plastic toughness.
Applications:
As a low cost stainless steel, 1Cr13 is widely used in machinery manufacturing. It is usually used to manufacture oxidation resistant components below 800℃, such as gas turbine blades, mechanical parts of various pumps, shafts and [TJC STEEL]pull rods of steam equipment, etc.Because of its good corrosion resistance, it is also used as a cutting tool.

Comments are closed.

      TJC Steel News Center

    Company News, Market News and Order Cases About TJC Steel.

    Archives

    March 2023
    February 2023
    January 2023
    December 2022
    November 2022
    September 2022
    July 2022
    May 2022
    March 2022
    February 2022
    January 2022
    December 2021
    November 2021
    October 2021
    September 2021
    August 2021
    July 2021
    June 2021
    April 2021
    March 2021
    February 2021
    January 2021
    December 2020
    November 2020
    July 2020
    June 2020
    May 2020
    April 2020
    March 2020
    February 2020
    January 2020
    December 2019
    November 2019
    October 2019
    September 2019
    May 2019
    April 2019
    January 2019
    December 2018
    October 2018
    September 2018
    August 2018

    Categories

    All
    Stainless Coils/ Sheets
    Steel PIpe
    Steel Plates

    RSS Feed

HOME

ABOUT

PRODUCT

NEWS

CONTACT

TJC IRON& STEEL CO.,LTD
Tel:+86-371-86107816; +8613674998777 Email: Info@tjcsteel.com
HENAN SCALE IMP&EXP CO.,LTD
ZHENGZHOU ZHIYUAN IMP&EXP CO.,LTD
Copyright © 2015
  • Home
  • Product
  • Contact
  • About
  • News