09Cr17Ni5Mo3N, UNS S35000, 633 Precipitated Hardened Stainless Steel- TJC STEEL.

​633 Stainless Steel is precipitated hardened stainless steel, can be subjected to low temperature heat treatment to obtain different levels of strength, [TJC STEEL]for high strength and excellent weldability and corrosion resistance occasions.

Standard:
CHINA GB/T 20878-2007 09Cr17Ni5Mo3N
S51750
AMERICA ASTM A693-2003 S35000，633
EUROPE EN 10088-1:2005[TJC STEEL] (1.4457)

Chemical Composition(%):
C 0.07~0.11 Cr 16.0~17.0 Ni 4.00~5.00
Si ≤0.50 P ≤0.040 Mo 2.50~3.20
Mn 0.50~1.25 S ≤0.030[TJC STEEL] N 0.07~0.13

Grades:
AMERICA ATI Metals AM 350®
JAPAN TOKKIN TOKKIN® 350

Material Characteristics:
The corrosion resistance of martensitic stainless steels is better than that of other martensitic stainless steels which can be quenched and hardened. [TJC STEEL]In most media, the corrosion resistance of martensitic stainless steels is comparable to that of 316 type stainless steels.
② High strength.After heat treatment according to national standard specification, hardness ≥36HRC or ≥42HRC can be obtained.
③ It is easier to weld than other stainless steels that can be precipitated and hardened. It can be welded by traditional inert gas method.

Applications
633Stainless Steel is commonly used in applications up to 1000°F (537 ° C) where strength and good corrosion resistance are required, such as [TJC STEEL]gas turbine compressor components (blades, plates, rotors and shafts), and similar components requiring high strength at room and moderate temperatures;Precision seals, couplings for semiconductor processing equipment and high vacuum systems;Aerospace applications requiring high strength edge welded bellows, etc.