06Cr13 (0Cr13),410S,SUS410S,1.4000 Martensitic (Ferrite) Stainless Steel- TJC STEEL.

​06Cr13, the American standard 410S, is the lowest carbon content in the Cr13 martensitic stainless steel.Due to the microstructure of[TJC STEEL] the matrix under annealing condition, it is also classified as ferritic stainless steel in a few standards.

Standard Control
CHINA GB/T 20878-2007 S41008 06Cr13
（0Cr13）
GB/T 24511-2009 S11306
AMERICA ASTM A240-15a S41008,410S
JAPAN JIS G 4304:2005 SUS410S
GERMANY DIN EN 10088-2:1995[TJC STEEL] X6Cr13,1.4000

Component Specification
GRADE 06Cr13* 410S SUS410S 1.4000
C ≤0.08 ≤0.08 ≤0.08 ≤0.08
Si ≤1.00 ≤1.00 ≤1.00 ≤1.00
Mn ≤1.00 ≤1.00[TJC STEEL] ≤1.00 ≤1.00
P ≤0.040 ≤0.040 ≤0.040 ≤0.040
S ≤0.030 ≤0.030 ≤0.030 ≤0.015
Cr 11.5~13.5 11.5~13.5 11.5~13.5 12.0~14.0
Ni (≤0.60) ≤0.60 (≤0.60) --
*：S41008 is listed in the table, while S11306 is slightly different in composition.

Mechanical Property
Density（g/cm3）20℃[TJC STEEL] 7.75
Specific heat [kJ/(kg·K)]  0~100℃ 0.46
Heat conductivity [W/(m·K)] 100℃ 25.0
coefficient of linear expansion（10-6/K） 0~100℃ 10.6
0~500℃ 12.0
specific resistance（Ω·mm2/m）20℃ 0.60
longitudinal modulus of elasticity（kN/mm2）20℃ 220
magnetism Y

Mechanical Property

Dimensions of sample hairs（mm） ≤75
heat treating regime anneal[TJC STEEL] 800 ~ 900 ℃ slow cooling
Or about 750℃ fast cooling

quench 950 ~ 1000 ℃ cold oil
temper 700~750℃cold oil
Mechanical properties 
(quenching + tempering)
Specified non-proportionality
Extension strength MPa ≥345
strength of extension MPa ≥490
Percentage elongation after fracture % ≥24
Percentagereduction of area; reduction of area ≥60
The hardness of delivery HBW anneal ≤183

Material Characteristics:
(1) The corrosion resistance and corrosion resistance are similar to 1Cr13 (410) and better, in low concentration of mild organic and [TJC STEEL]inorganic acid, alkali and some chemical conditions have corrosion resistance.
(2) Good oxidation resistance, sustainable use in 705℃ environment.
(3) good plastic toughness, easy to be formed by rotation, bending and rolling.
(4) It can be welded by common fusion and resistance technology.

Applications:
The main product form [TJC STEEL]is plate, used for structural parts such as automobile muffler and exhaust system components, but also widely used in containers, heat exchangers, underground pipes, etc.