20Cr1Mo1VNbTib High Temperature Bolt Steel- TJC STEEL.

20Cr1Mo1VNbTiB China's self-developed low alloy high strength steel, also [TJC STEEL]known as Zhengqi No.1 steel.

Relevant Standards:
GB/T 20410-2006 "high temperature bolts for turbine steel"
DL/T 439-2018 "Technical guidelines for high-temperature fasteners in thermal power plants"
DL/T 715-2015 "Guidelines for Selection [TJC STEEL]of Metal Materials in Thermal Power Plants"

Chemical Composition（%）（GB/T 20410-2006）
C 0.17~0.23 Cr 0.90~1.30
Si 0.40~0.60 Mo 0.75~1.00
Mn 0.40~0.65 V 0.50~0.70
P ≤0.025 Nb 0.11~0.22
S ≤0.025 Ti 0.05~0.14
Ni ≤0.30[TJC STEEL] B 0.001~0.004
Cu ≤0.25

Heat Treatment:
1020~1040℃ Oil Cooling，700~720℃ Tempering for 6h and then air cooling.

Mechanical Property（GB/T 20410-2006）
Sample Size（mm） Ø25
Heat Treatment Quenched（Oil,Water Cooling/℃ 1020~1040
Tempered（Air Cooling）/℃ 690~730
Mechanical Property TS Rm/MPa[TJC STEEL] ≥785
YS Rp0.2/MPa ≥670
A/% ≥14
Z/% ≥50
AKU2/J ≥39
Hardness HBW 10/3000 255~305

  Property:
1.Good high temperature performance, high durable strength and plasticity, good anti-relaxation performance, small thermal brittle tendency, low notch sensitivity.
2.Heat treatment is more [TJC STEEL]sensitive, such as improper thermal processing control, easy to appear naked eye coarse grain, so there are strict grain size acceptance standards for different design grades.
The highest operating temperature is 570℃.

Application:
20Cr1Mo1VNbTiB bainite [TJC STEEL]heat resistant steel has excellent comprehensive properties and is mainly used as high temperature bolts in thermal power plants below 570℃. It is widely used in large and medium-sized units in thermal power plants.